Part two of a series of articles exploring the esthetics of a Class IV direct composite restoration.


In part one of this series, we discussed how clear understanding of the Class IV direct restoration is the gateway to all knowledge of direct bonding in the anterior dentition. We also discussed the case of a female patient in her early twenties with esthetic complaints and a diagnosis of altered passive eruption (APE) and tooth surface loss (TSL).

In this article, we will discuss the ideal preparation stages of the tooth prior to bonding. To illustrate, we will discuss the case of a 21-year-old male who presented with TSL related to nocturnal bruxism. His complaints were mainly esthetic regarding the lateral incisors and canines (Fig 1).

Figure 1: The patient's esthetic complaints regarded the lateral incisors and canines.
Figure 1: The patient's esthetic complaints regarded the lateral incisors and canines.

Due to the patient's age, a decision was made to treat him with a purely additive approach with direct composite resin of the upper and lower anterior sextants alongside an occlusal equilibration.

Figure 2: The teeth were isolated with a rubber dam and floss ties.
Figure 2: The teeth were isolated with a rubber dam and floss ties.
Figure 3: The missing tooth structure was replaced with direct composite resin in layers using the Natural Layering Approach, Dietschi.
Figure 3: The missing tooth structure was replaced with direct composite resin in layers using the Natural Layering Approach (Dietschi)
Figure 4: The immediate post-operative appearance after polishing.
Figure 4: The immediate post-operative appearance after polishing.

The figures below highlight the new occlusal scheme in protrusive (Fig. 5) from canine guidance to crossover (Fig. 6 and 7).

Figure 5: The new occlusal scheme in protrusive.
Figure 5: The new occlusal scheme in protrusive.
Figure 6: The new occlusal scheme from canine guidance.
Figure 6: The new occlusal scheme from canine guidance.
Figure 7: The new occlusal scheme from canine guidance to crossover.
Figure 7: The new occlusal scheme from canine guidance to crossover.

Small Class IV restorations like the case illustrated above cause practitioners the most issues with repeated debonds. In this article, we will consider a protocol for predictable bonding to tooth structure (both enamel and dentin) prior to layering the Class IV restoration. This protocol is common to all bonding and can be employed for any anterior direct procedure.

Particle abrasion

Particle abrasion – sometimes known as air abrasion – in dentistry was first developed in the 1940s by Dr. Robert Black. This was further improved and combined with adhesive technology by Dr. J. Tim Rainey in the United States. Dr. Rainey could be considered the father of modern microdentistry.

Particle abrasion is defined as, “the process of tooth substrate removal utilizing the kinetic energy from particles entered in a high velocity stream of gas +/- fluid.”1 The gas is usually compressed air from the delivery cart and is sometimes augmented with water or water/alcohol mix.

I prefer the addition of an alcohol/water mix – also called hydro-abrasion – since fewer particles are required for the abrasion. Importantly, the process is also cleaner with less dust contamination of surrounding air.

Reduced dust is healthier for the operator and less damaging to surrounding equipment such as handpieces, microscopes and camera gear. Examples of available hydro-abrasion units include Velopex Aquacare and PrepStart H2O.

The particles commonly employed for restorative dentistry are aluminum oxide, glycine and SYLC. Aluminum oxide is most used since it offers sharp, irregular particles of the required hardness at a low cost.


Remember -

Kinetic energy = ½ MV2

M = mass, V = velocity.

It therefore follows that increased cutting efficiency will be gained by:

  1. Greater particle mass
  2. Increased velocity of the particles resulting from either higher air pressure, narrower bore of delivery tip or the tip being closer to the tooth structure1

I use 27-micron alumina at a pressure of around 2-3 bar. When using the unit, the tip is held close to the tooth, but is continually in motion – dwelling in one area increases the degree of cutting. The motion used is a crisscross, checkerboard shaped movement.

Particle abrasion improves bond strengths and restoration longevity as a result of:

  1. Removal of biofilm such as plaque, calculus and staining<
  2. Removal of old composite bonding
  3. Removal of the aprismatic layer of enamel

What is the aprismatic layer?

All enamel surface layers are comprised of amorphous, highly fluoridated, remineralised enamel around 10-30 microns in thickness – this is the aprismatic layer.

When we eat sugars, our oral biofilm creates acids. This acid attacks the tooth surface: the so-called “carious challenge.” This results in the loss of hydroxyapatite from the surface of our enamel (demineralization). Fortunately, most of us have fluoride in our diet or in toothpastes, mouthwashes and floss. The fluoride demineralizes the enamel, creating the aprismatic layer. The aprismatic layer lacks prism structure and is therefore more resistant to future acid attack.

As restorative dentists we aim to etch teeth with 35 – 37 percent phosphoric acid to bond to them – but the aprismatic layer makes this less effective. Additionally, the aprismatic layer is only loosely adherent to the underlying main body of enamel. This means that when we bond to aprismatic enamel, we can achieve weak bonds.

However, heat is generated when we begin to polish the restoration because of friction between the polishing rubber/disc and the tooth/restoration surfaces. Each of the components of the tooth-restoration interface – including enamel, dentin, bonding agent and composite resin – have a different coefficient of thermal expansion (CTE). This means they expand and contract at different rates when heated.

As a result of the CTE mismatch, the weakest link in the system often breaks down during the polishing process. This is commonly the link between the aprismatic enamel and the underlying enamel. On a clinical level, this is why a white line may appear during the polishing process that was not present prior to polishing. Particle abrasion reduces this risk.

Sharp cavosurface angles create stress risers. A stress riser is an area of high stress concentration which may result in adhesive bond breakdown. Particle abrasion creates rounded cavosurface angles.

Figure 8:
Figure 8: “Fanning” of adhesive particles as they exist the orifice of the instrument tip.

Rounding of the margins is caused by “fanning” of the adhesive particles as the exit the orifice of the instrument tip (Fig. 8). However, abrasion provided by the peripheral portion of the stream is less efficient due to the lower velocity and concentration of alumina particles. This results in the rounding of all internal line angles.

This effect is minimized when the tip is sited less than 1.0mm from the tooth where fanning is negligible. Therefore, for any preparation requiring a rounded cavosurface margin, the instrument tip should be placed 2.0mm from the tooth surface. If a butt joint is required, a distance of 0.5mm should be employed.2

There is a wealth of research both in vitro and in vivo which demonstrates an increase in bond strengths to enamel after particle abrasion.3 4 5 6 However, the effects on dentin bonding are more controversial. Particle abrasion reduces smear layer thickness in comparison to burr prepared dentin. Since they contain weaker acids and are less able to penetrate the smear layer, the performance of self-etching bonding agents may be improved.7 This effect is not seen in etch and rinse dentin bonding agents.

In contrast, particle abrasion may result in splitting of the collagen fibers on the dentin surface, reducing the quality of the hybrid layer.8 Anecdotally, I have used lower mass particles at low pressures for 15 years with no discernible adverse effects.

Figure 9: Tofflemire bands without the matrix bands interproximal.
Figure 9: Tofflemire bands without the matrix bands interproximal.

It is prudent to protect the adjacent teeth when carrying out particle abrasion and bonding procedures to avoid iatrogenic damage and linking the teeth together. I tend to employ Tofflemire bands without the matrix bands interproximal (Fig. 9). Note the matte appearance of the enamel surface following hydro-abrasion.

Tooth preparation with burrs

Following particle abrasion, the tooth is prepared on the facial and interproximal surfaces.

Figure 10: A coarse or medium diamond flame shaped burr (863) is used to create a 2.0mm long bevel extending from the enamel-dentin junction superiorly to a knife edge within the enamel inferiorly.
Figure 10: A coarse or medium diamond flame shaped burr (863) is used to create a 2.0mm long bevel extending from the enamel-dentin junction superiorly to a knife edge within the enamel inferiorly.
Figure 11: The inferior and superior borders of the bevel.
Figure 11: The inferior and superior borders of the bevel.

Facial -

A coarse or medium diamond flame shaped burr (863) is used to create a 2.0mm long bevel extending from the enamel-dentin junction superiorly to a knife edge within the enamel inferiorly (Fig. 10). The bevel has an inferior and superior border (Fig. 11) – this is discussed in more detail in the final article in this series.

Key advantages of the bevel:

  1. The bevel provides an increased surface area for bonding improving retention.
  2. From an esthetic standpoint, when layering over the bevel there is a greater capacity to create an invisible margin in comparison to a butt joint.

A coarse/medium diamond has the advantage of efficiency when creating the bevel. However, the large particles on the burr tend to cause microfractures of the enamel at the cavosurface.

Remember that composite resin contracts as it polymerizes (polymerization shrinkage) and sets up stresses. These stresses may cause breakdown of the weakest link – often between the fractured enamel prisms and the main body of the enamel. Consequently, fractured enamel prisms pull away with the contracting composite. This is called the “enamel peel concept” and is a cause of white lines at the restoration margin.

Restorative dentists can avoid this problem by finishing the bevel at extremely low speed (3000 RPM) and water spray with a flame carbide finishing burr – this will reduce the number of fractured prisms. Practitioners should avoid polishing with a silicone point because silicone debris may remain – this results in decreased bond strengths.

Interproximal -

The mesial and distal interproximal surfaces are finished with a metal finishing strip. These are available from Brassler, GC and Cosmedent, amongst others. This will remove staining, old composite resin, biofilm and the aprismatic layer. This step will mean the restoration is less likely to stain interproximal in the mid-term. The transition from incisal edge to interproximal is rounded off with a medium disc (e.g. Soflex, 3M) to remove sharp line angles and reduce stress.

Palatal -

Figure 12: Correctly finished MID and MI preparations.
Figure 12: Correctly finished MID and MI preparations.

The palatal margin is finished as a simple butt joint. Correctly finished MID and MI preparations are seen clinically in Figure 12. Explore bonding and layering the Class IV Restoration in the next and final article in this series.

 

Jason Smithson, BDS (Lond), DipRestDentRCS (Eng), is a member of Spear Resident Faculty.

 

References

  1. Byyant CL. The role of air abrasion in preventing and Treating Early Pit and Fissure Caries. J. Can Dent Assoc.1999; 65:566-569.
  2. Nayak D, Ignatius G, Shenoy A, Nayak SD. Minimal Intervention Dentistry: Air Abrasion. Heal Talk. Mar/Apr 2013; 5(4): 12-13
  3. Laurell K, Lord W, Beck M. Kinetic cavity preparation effects on bonding to enamel and dentin (abstract 1437) J Dent Res. 1993;72:283.
  4. Keen DS, von Frauhofer JA, Parkins FM. Air-abrasive “etching”: Composite bond strengths (abstract 238) J Dent Res. 1994;73:131.
  5. Berry EA, Ward M. Bond strength of resin composite to air-abraded enamel. Quintessence Int. 1995; 26:559–62.
  6. Yazici AR, Kiremitci A, Celik C, Ozgunaltay G, Dayangac B. A Two-Year Clinical Evaluation of Pit and Fissure Sealants Placed with And Without Air Abrasion Pretreatment in Teenagers. JADA Oct 2006; 13(10): 140-5.
  7. Laurell KA Hess JA. Scanning electron micrographic effects of air-abrasion cavity preparation on human enamel and dentin, Quintessence Int 1995; 26:139-144.
  8. Nikaido T, Yamada T, Koh Y, Burrow MF, Takatsu T. Effect of air-powder polishing on adhesion of bonding systems to tooth substrates. Dent Mater 1995; 11: 258-264.